CuZn15 / C23000 / CW502L / H85 Alloy Brass Bar Diameter 4 - 200mm Custom Cutting
| Product | Brass Bar,Brass Rod,Brass Shaft,Brass Stick. |
| Standard | ASTM,AISI,EN,BS,JIS,GB/T,BSI,AS/NZS,ISO,etc. |
| Material | H96,H90,H85,H80,H70,H68,H65,H63,H62,H60,C21000,C22000,
C23000,C24000,C26000,C26800,C27000,C27200,C28000,C35000,etc.Or as required. |
| Surface-mount | mill,polished,bright,oiled,or as required. |
| Density | 8.5g/cm3 |
| Diameters | 1-200mm |
| Hardness | 1/16 hard,1/8 hard,3/8 hard,1/4 hard,1/2hard,full hard,soft,etc. |
| Shape | Square,Rectangular,Round . |
| Length | 500-6000mm,or as required. |
| Package | Standard Sea-worthy package , fixed by belt then loaded into fumigated
wooden box . |
| Container Size | 20Gp - 2.352(width) *2.385 ( Height ) * 5.90 ( Inside length ) Meter |
| 40Gp - 2.352(width) *2.385 ( Height ) * 11.8 ( Inside length ) Meter |
| 40HQ - 2.352(width) *2.69 ( Width ) * 5.90 ( Inside length ) Meter |
| Port of shipment | Tianjin Xingang port , Qingdao port , Shanghai port , ningbo port ,
Guangzhou port ,etc. |
Brass is a term that refers to a wide range of copper-zinc alloys with different properties that include machinability, strength, hardness, wear-resistance, ductility, corrosion-resistance, antimicrobial, electrical and thermal conductivity and color.
Brasses are available in a wide range of colors such as yellow, red, silver and gold etc. These colored brasses, which can be easily shaped, are used by designers and architects in order to improve the inside and outside appearances of buildings.
UNS C23000 brass alloys are red in color and stronger than C22000 alloys. The following datasheet provides an overview of UNS C23000 red brass alloys.
Chemical Composition
The chemical composition of UNS C23000 red brass alloys is outlined in the following table.
| Element | Content (%) |
| Cu | 85 |
| Zn | 15 |
Physical Properties
The following table shows the physical properties of UNS 23000 red brass alloys.
| Properties | Metric | Imperial |
| Melting point-liquidus | 1027°C | 1880°F |
| Melting point-solidus | 988°C | 1810°F |
| Density (@20°C/68°F) | 8.75 gm/cm3 | 0.316 lb/in3 |
Mechanical Properties
The mechanical properties of UNS C23000 red brass alloys are displayed in the following table.
| Properties | Metric | Imperial |
| Tensile strength | 269-724 MPa | 39-105 ksi |
| Yield strength | 69-434 MPa | 10-70 ksi |
| Elongation | 55% | 55% |
| Poisson's ratio | 0.34 | 0.34 |
| Elastic modulus | 117 GPa | 16969 ksi |
Other Designations
Equivalent materials to UNS 23000 red brass alloys are given in the table below:
| ASME B16.22 | ASTM B134 | ASTM B687 | ASTM B111 |
| ASME B16.29 | ASTM B135 | ASTM B698 | ASME SB543 |
| ASME SB111 | ASTM B359 | MIL T-20168 | ASTM B587 |
| ASME SB359 | ASTM B36 | QQ W321 | ASTM B543 |
| ASME SB395 | ASTM B395 | SAE J461 | |
| ASME SB43 | ASTM B43 | SAE J463 | |
| | | | |
Fabrication and Heat Treatment
Annealing
UNS C23000 red brass alloys are annealed between 426 and 732°C (800 and 1350°F).
Cold Working
UNS C23000 brass alloys have excellent cold working capacity.
Welding
The welding processes used for UNS C23000 brass alloys include brazing, gas shielded arc welding, soldering, butt welding and spot welding. Coated metal arc welding and seam welding are not recommended for this brass alloy.
Forging
UNS C23000 brass alloy can be forged between 788 and 899°C (1450 and 1650°F).
Machinability
UNS C23000 brass alloys have a machinability rating of 30.
Hot Working
UNS C23000 brass alloys have good hot forming capacity.
Applications
UNS C23000 brass alloys are used for jewelry, cold-formed hardware and electrical components, fittings, decorative chains and dezincification-resistant fasteners.