Alloy 800h / 800HT Nickel Alloy Plate Sheet Width 1000mm 1219mm 1500mm Nickel Alloy

Name: Alloy 800h 800HT Nickel Alloy Plate Sheet Width 1000mm 1219mm 1500mm Nickel Alloy
Brand: DELTA
Price: 40 USD

Alloy 800h / 800HT Nickel Alloy Plate Sheet Width 1000mm 1219mm 1500mm Nickel Alloy Manufactures

Brand Name : DELTA

Model Number : UNS N08810 / 1.4958

Certification : ISO

Place of Origin : China

MOQ : 500 kgs

Price : 40-45 USD/Kg

Payment Terms : L/C, T/T, Western Union

Supply Ability : 3 Ton per week

Delivery Time : 5 - 12 days based on the quantity

Packaging Details : standard packing for export

Products : Nickel Alloy Sheet & Plate

Grade : UNS N08810

Thickness : 0.5 - 30.0mm

Standard size : 1000*2000mm 1219*2438mm

Standard : ASTM EN

Service : Cutting

Loading Port : Shanghai Port

Surface : 2B NO.1 NO.4 NO.8

Contact Now

Alloy 800h / 800HT Nickel Alloy Plate Sheet Width 1000mm 1219mm 1500mm Nickel Alloy

Material	Monel/Inconel/Hastelloy/Duplex Steel/PH Steel/Nickel Alloy
Shape	Round,Forging,Ring,Coil,Flange,Disc,Foil,Spherical,Ribbon,Square,Bar,Pipe,Sheet
Grade	Duplex: 2205(UNS S31803/S32205),2507(UNS S32750),UNS S32760(Zeron 100),2304,904L
	Others:253Ma,254SMo,654SMo,F50(UNSS32100)F60,F61,F65,1J22,N4,N6 etc
	Alloy : Alloy 20/28/31
	Hastelloy:HastelloyB/ -2/B-3/C22/C-4/S/ C276/C-2000/G-35/G-30/X/N/g
	Hastelloy B / UNS N10001,Hastelloy B-2 / UNS N10665 / DIN W. Nr. 2.4617,Hastelloy C, Hastelloy C-4 / UNS N06455 / DIN W. Nr. 2.4610,Hastelloy C-22 / UNS N06022 / DIN W. Nr. 2.4602, Hastelloy C-276 / UNS N10276 / DIN W. Nr. 2.4819,Hastelloy X / UNS N06002 / DIN W. Nr. 2.4665
	Haynes: Haynes 230/556/188
	Inconel 600/601/602CA/617/625/713/718/738/X-750,Carpenter 20
	Inconel 718 / UNS N07718 / DIN W. Nr. 2.4668,Inconel 601 / UNS N06601 / DIN W. Nr. 2.4851, Inconel 625 / UNS N06625 / DIN W. Nr. 2.4856,Inconel 725 / UNS N07725,Inconel X-750 / UNS N07750 / DIN W. Nr. 2.4669,Inconel 600 / UNS N06600 / DIN W. Nr. 2.4816
	Incoloy: Incoloy 800/800H/800HT/825/925/926;
	GH: GH2132,GH3030,GH3039,GH3128,GH4180,GH3044
	Monel: Monel 400/K500/R405
	Nitronic: Nitronic 40/50/60;
	Nimonic: Nimonic 75/80A/90/A263 ;
Specification	Wire: 0.01-10mm Strip: 0.055.0-5.0250mm Bar: φ4-50mm;Length 2000-5000mm Pipe: φ6-273mm;δ1-30mm;Length 1000-8000mm Sheet: δ 0.8-36mm;Width 650-2000mm;Length 800-4500mm
Product Characteristics	1.According to the preparation process can be divided into deformation superalloys, casting superalloys and powder metallurgy superalloys. 2.According to the strengthening mode, there are solid solution strengthening type, precipitation strengthening type, oxide dispersion strengthening type and fiber strengthening type, etc..
Standard	GB,AISI,ASTM,DIN,EN,SUS,UNS etc
Inspection	ISO,SGS,BV and so on.

Alloys 800H/HT UNS N08810 / UNS N08811 / W.NR. 1.4959

Alloys 800H® and 800HT® are iron-nickel-chromium solid solution strengthened alloys with a nominal chemical composition of 42% iron, 34% nickel, and 22% chromium. These two grades are variations of the base grade 800 and are referred to by the tradenames Incoloy® 800H and Incoloy® 800HT and the universal designation UNS N08810 and N08811, respectively. 800H® and 800HT® share the high-temperature oxidation and carburization resistance of Alloy 800 but have enhanced creep and stress rupture properties.

CHEMICAL COMPOSITION

The base composition of 800H/HT® is identical to the parent Alloy 800. However, in both 800H® and 800HT®, the levels of carbon, aluminum, and titanium are modified for improved creep resistance. The base 800 grade has a carbon range of 0 - 0.10%, while 800H® raises the minimum carbon level to 0.05%. Similarly, the base 800 grade has a combined aluminum and titanium content requirement of 0.30 - 1.20%, while 800HT® raises the minimum Al + Ti level to 0.85% and increases the minimum carbon to 0.06%.

CORROSION RESISTANCE

Both grades share the corrosion resistant characteristics of the base grade Alloy 800, including good general corrosion resistance, as well as good resistance to reducing and oxidizing acids, organic acids, seawater, salts, and particularly excellent resistance to nitric acid. Alloy 800H and 800HT also exhibit excellent corrosion resistance to chloride stress corrosion cracking (SCC). However, alloys 800H and 800HT are not recommended for sulfuric acid service. Additionally, they are susceptible to chromium carbide precipitation along grain boundaries when subjected to temperatures in the range of 1000°F - 1400°F (538°C - 760°C).

ELEVATED TEMPERATURE RESISTANCE

800H and 800HT have outstanding resistance to oxidation, carburization, and sulfidation at temperatures up to 1800°F.

MECHANICAL PROPERTIES

800H and 800HT are typically supplied in a low-strength solution annealed condition. While intended for high-temperature applications, they have excellent toughness down to cryogenic temperatures.

HEAT TREATMENT

Alloys 800H and 800 HT cannot be strengthened by heat treating. They are typically solution annealed at 2050°F - 2150°F (1121°C - 1177°C) followed by rapid cooling. Stress-relieving at 1000°F - 1600°F (538°C - 870°C) may also be performed after cold working to reduce residual stresses and prevent distortion.

WORKABILITY

Alloy 800H and 800HT can be cold worked using common methods and should be in the annealed condition prior to cold working. The large grain size produced in both grades from solution annealing can lead to “orange peel” surface roughening after cold working. Hot-working should be done above 1600°F (871°C).

APPLICATIONS

Alloy 800H® and 800HT® are used at temperatures from 1100°F – 1800°F (593°C – 982°C) where creep and stress rupture failure is a concern. 800H® is typically used at the lower end of this range, while 800HT® is employed at the upper end. Applications include structural members, furnace equipment, heat exchangers, petrochemical vessels and piping, and aerospace. CRA offers specialty alloy 800H/HT® seamless pipe & tube for use in multiple industries and applications, including:

Furnace Equipment
Aerospace
Petrochemical Vessels & Piping

Chemical Composition

UNS Designation	N08800	N08810	N08811
Incoloy Alloys	800	800H	800HT
Nickel	30.0 - 35.0	30.0 - 35.0	30.0 - 35.0
Chromium	19.0 - 23.0	19.0 - 23.0	19.0 - 23.0
Iron	39.5 min.	39.5 min	39.5 min.
Carbon	0.10 max	0.05 - 0.10	0.06 - 0.10
Aluminum	0.15 - 0.60	0.15 - 0.60	0.25 - 0.60
Titanium	0.15 - 0.60	0.15 - 0.60	0.25 - 0.60
Aluminum + Titanium	0.30 - 1.20	0.30 - 1.20	0.85 - 1.20
ASTM Grain Size	Not Specified	5 or Coarser	5 or Coaser

Alloy 800h / 800HT Nickel Alloy Plate Sheet Width 1000mm 1219mm 1500mm Nickel Alloy

Product Tags: